DAIAMID<\/p>\n
Polyplastics-Evonik<\/p>\n
Japan<\/p>\n
Bicycle parts, gears, valve housings, filter housings, gearbox housings.<\/p>\n
| Property<\/th> | Grade<\/th> | Density \n(g\/cm\u00b3)<\/th> | Tensile strength \n(MPa)<\/th> | Tensile Modulus \n(MPa)<\/th> | Strain at break(%)<\/th> | HDT \n(0.45 MPa)<\/th> | Charpy notched impact strength \n(kJ\/m\u00b2)<\/th> | Note<\/th>\n<\/tr>\n<\/thead>\n |
|---|---|---|---|---|---|---|---|---|
| Standard<\/td> | D16<\/td> | 1.07<\/td> | 62<\/td> | 1800<\/td> | >50<\/td> | 140\u00b0C<\/td> | 5<\/td> | Suitable for injection \/Filament extrusion<\/td>\n<\/tr>\n |
| High viscosity<\/td> | D22<\/td> | 1.07<\/td> | 55<\/td> | 1700<\/td> | >50<\/td> | 140\u00b0C<\/td> | 12<\/td> | <\/td>\n<\/tr>\n |
| Rapid crystallization<\/td> | D1643<\/td> | 1.07<\/td> | 62<\/td> | 1700<\/td> | >50<\/td> | 140\u00b0C<\/td> | 5<\/td> | Suitable for small injection molded parts<\/td>\n<\/tr>\n |
| TPU bonding<\/td> | ZX2900<\/td> | 1.07<\/td> | 55<\/td> | 1700<\/td> | >50<\/td> | 140\u00b0C<\/td> | 8<\/td> | <\/td>\n<\/tr>\n |
| Glass Fiber \nReinforced<\/td> | ZX2900GF20<\/td> | 1.23<\/td> | 110<\/td> | 6000<\/td> | >3<\/td> | 210\u00b0C<\/td> | 10<\/td> | TPU bonding<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n\nReinforced grade Molding conditions<\/h2>\nPre-drying : 80\u00b0C ~ 90\u00b0C x 4hr Non-reinforced grade Molding conditions<\/h2>\nPre-drying : 80\u00b0C ~ 90\u00b0C x 2~4hr Brand DAIAMID Manufacturer Polyplastics-Evonik Point of origin Japan Characteristics Low moisture absorbability Excellent chemical resistance Resistant to abrasion Far superior strength and dimensional stability compared to PA6 and PA66 Higher hardness and strength than PA12 TPU injection molding specification available Applications: Bicycle parts, gears, valve housings, filter housings, gearbox housings. TDS Table Reinforced grade Molding …<\/p>\n |